Microstructure and mechanical properties of multilayered steel | |
Zhao, Xiaokang1; Cao, Rui1; Zhang, Xiaobo1; Zhang, Ruihua2; Chen, Jianhong1 | |
2018-01-25 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution |
ISSN | 0253360X |
卷号 | 39期号:1页码:45-49 |
摘要 | Microstructure and corresponding mechanical properties of multilayered steel were revealed by SEM observation and analysis of tensile and bending properties. Analysis results show that the tensile strength of multilayered steel is 966 MPa, the elongation is 17% and this material exhibits excellent bending properties, the bending strength is 5 452 MPa, bending deflection is 22 mm when the multilayered steel is bent to 136°. From the tensile fracture and the microscopic appearance of bending to 180°, it can be found that brittle cracking appeared in big block phase of middle layer and dimple fracture characteristics appeared at matrix during the fracture process, delamination cracking were easily induced in the interface between Ni layer and the middle layer; However, there were satisfied interface between the martensitic layer of on both sides and the Ni layer, and a lot of plastic deformation with dimple morphology were produced in the interface between the martensitic layer of on both sides and the Ni layer with during the tension and produced in bending. © 2018, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved. |
关键词 | Bending (forming) Bending strength Cracks Fracture Microstructure Morphology Tensile properties Tensile strength Bending deflection Bending properties Fracture process Fracture surfaces Microscopic appearances Microstructure and mechanical properties Multi-layered Tensile fractures |
DOI | 10.12073/j.hjxb.2018390011 |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20182205263419 |
EI主题词 | Bending (deformation) |
EI分类号 | 531.2 Metallography - 535.2 Metal Forming - 951 Materials Science |
来源库 | Compendex |
分类代码 | 535.2 Metal Forming - 951 Materials Science |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/114495 |
专题 | 材料科学与工程学院_特聘教授组 材料科学与工程学院 |
作者单位 | 1.Lanzhou University of Technology, State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou; 730050, China; 2.Institute of Research of Iron and Steel, Beijing; 100081, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Zhao, Xiaokang,Cao, Rui,Zhang, Xiaobo,et al. Microstructure and mechanical properties of multilayered steel[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2018,39(1):45-49. |
APA | Zhao, Xiaokang,Cao, Rui,Zhang, Xiaobo,Zhang, Ruihua,&Chen, Jianhong.(2018).Microstructure and mechanical properties of multilayered steel.Hanjie Xuebao/Transactions of the China Welding Institution,39(1),45-49. |
MLA | Zhao, Xiaokang,et al."Microstructure and mechanical properties of multilayered steel".Hanjie Xuebao/Transactions of the China Welding Institution 39.1(2018):45-49. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论