Analysis of welding-brazing joints of Ti/Al dissimilar metals obtained by cold metal transfer method | |
Sun, Junhao; Cao, Rui; Chen, Jianhong | |
2015-03-25 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution |
ISSN | 0253360X |
卷号 | 36期号:3页码:51-54 |
摘要 | Cold metal transfer (CMT) welding-brazing of Al6061 and TA2 was carried out using ER4043 filler metal. The microstructure characteristics of the Ti/Al joints were analyzed by optical microscopy, scanning electron microscopy and energy dispersive spectrometer, respectively. Mechanical properties of the joints were characterized by measurement of the tensile strength. The results indicate that a welding-brazing joint was formed by CMT method, which included a welding joint at the aluminium sheet side and a brazing joint at the titanium sheet side. The intermetallic compound at the brazing interface consisted of two different layers. Among them, the continuous layer near titanium substrate was composed of Ti3Al intermetallic compound, while the serration-shaped layer next to the weld metal was composed of TiAl3 intermetallic compound. When groove angle 30° of titanium sheet was used during the welding process, uniform intermetallics would be formed at the brazing interface, thus sound joint which had a tensile strength of 197.5 MPa was obtained and the failure location of this joint was at Al HAZ. ©, 2015, Hanjie Xuebao/Transactions of the China Welding Institution. All right reserved. |
关键词 | Aluminum alloys Binary alloys Brazing Dissimilar metals Filler metals Intermetallics Metals Scanning electron microscopy Spectrometers Tensile strength Titanium sheet Welding Cold metal transfers Continuous layers Energy dispersive spectrometers Failure locations Joint strength Microstructure characteristics Ti/Al dissimilar alloys Titanium substrates |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20151700776671 |
EI主题词 | Titanium alloys |
EI分类号 | 531 Metallurgy and Metallography - 538.1.1 Soldering - 538.2 Welding - 541.1 Aluminum - 541.2 Aluminum Alloys - 542.3 Titanium and Alloys - 741.3 Optical Devices and Systems |
来源库 | Compendex |
分类代码 | 531 Metallurgy and Metallography - 531.1 Metallurgy - 538.1.1 Soldering - 538.2 Welding - 541.2 Aluminum Alloys - 542.3 Titanium and Alloys - 741.3 Optical Devices and Systems |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/112430 |
专题 | 材料科学与工程学院_特聘教授组 材料科学与工程学院 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Sun, Junhao,Cao, Rui,Chen, Jianhong. Analysis of welding-brazing joints of Ti/Al dissimilar metals obtained by cold metal transfer method[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2015,36(3):51-54. |
APA | Sun, Junhao,Cao, Rui,&Chen, Jianhong.(2015).Analysis of welding-brazing joints of Ti/Al dissimilar metals obtained by cold metal transfer method.Hanjie Xuebao/Transactions of the China Welding Institution,36(3),51-54. |
MLA | Sun, Junhao,et al."Analysis of welding-brazing joints of Ti/Al dissimilar metals obtained by cold metal transfer method".Hanjie Xuebao/Transactions of the China Welding Institution 36.3(2015):51-54. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论