Microstructure, bonding mechanism and corrosion property of titanium TA2/copper T2 welded joint by cold metal transfer technology | |
Cao, Rui; Feng, Zhen; Chen, Jianhong; Jing, Min | |
2015-01-25 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution |
ISSN | 0253360X |
卷号 | 36期号:1页码:39-42 |
摘要 | This paper described a fundamental investigation of titanium TA2-copper T2 butt joint by cold metal transfer (CMT). During the welding process, wire was deviated from the edge of Cu sheet. A satisfied Ti-Cu CMT welding-brazing butt joint was obtained. Fusion welding joint was formed at copper side, while brazing joint was formed at titanium side. Welding-brazing joint was formed between titanium TA2-copper T2. Bonding mechanism of the welded joints was examined by scanning electron microscopy (SEM) with energy dispersive spectrometer (EDS) and tensile tests. Corrosion tests of Ti/Cu welded joint were conducted in solution of 10% HCl at room temperature. Results indicated that brazing interface consisted of various intermetallic compounds, i.e. Ti2Cu, TiCu, and AlCu2Ti. And the weld metal was composed of α-Cu solid solution and Ti-Cu-Al-Ni-Fe multi-phase. The tensile strength of the joint can reach to 205 MPa. There were corrosion grooves in brazing interfaces after corrosion for 7 days, and self-fracture after corrosion for 14 days. ©, 2015, Harbin Research Institute of Welding. All right reserved. |
关键词 | Aluminum alloys Binary alloys Brazing Butt welding Chlorine compounds Copper Corrosive effects Iron alloys Scanning electron microscopy Spectrometers Tensile strength Tensile testing Titanium Welds Bonding mechanism Brazing interface Brazing joints Cold metal transfers Corrosion property Corrosion tests Energy dispersive spectrometers Welding process |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20151400699856 |
EI主题词 | Titanium alloys |
EI分类号 | 531.2 Metallography - 538 Welding and Bonding - 539.1 Metals Corrosion - 541.1 Aluminum - 541.2 Aluminum Alloys - 542.3 Titanium and Alloys - 544.1 Copper - 545.1 Iron - 545.2 Iron Alloys - 741.3 Optical Devices and Systems |
来源库 | Compendex |
分类代码 | 538 Welding and Bonding - 539.1 Metals Corrosion - 541.2 Aluminum Alloys - 542.3 Titanium and Alloys - 544.1 Copper - 545.2 Iron Alloys - 741.3 Optical Devices and Systems |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/112348 |
专题 | 材料科学与工程学院_特聘教授组 材料科学与工程学院 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Cao, Rui,Feng, Zhen,Chen, Jianhong,et al. Microstructure, bonding mechanism and corrosion property of titanium TA2/copper T2 welded joint by cold metal transfer technology[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2015,36(1):39-42. |
APA | Cao, Rui,Feng, Zhen,Chen, Jianhong,&Jing, Min.(2015).Microstructure, bonding mechanism and corrosion property of titanium TA2/copper T2 welded joint by cold metal transfer technology.Hanjie Xuebao/Transactions of the China Welding Institution,36(1),39-42. |
MLA | Cao, Rui,et al."Microstructure, bonding mechanism and corrosion property of titanium TA2/copper T2 welded joint by cold metal transfer technology".Hanjie Xuebao/Transactions of the China Welding Institution 36.1(2015):39-42. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论