Mechanism of weld penetration increased by SiO2 in AC A-TIG welding for aluminum alloy | |
Huang, Yong; Fan, Ding | |
2008 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution |
ISSN | 0253360X |
卷号 | 29期号:1页码:45-49 |
摘要 | The weld penetration increased by SiO2 is the most obviously when some single-component fluxes are used as surface activating flux in AC A-TIG (alternating current activating-tungsten inert-gas) welding of aluminum alloy. The mechanism of SiO2 increasing weld penetration of AC A-TIG welding was studied. SiO2 has little effect on weld appearance of electron beam welding with positive defocus. A series of DCSP A-TIG welding experiments were carried out to investigate the effects of SiO2 on welding arc. It is found that SiO2 can constrict arc polarity area, broaden arc column and improve arc voltage. AC A-TIG welding with helium shielding gas was carried out. It is found that SiO2 constricts evaporation area, weakens evaporation of activating flux or base metal, and depresses weld pool surface. During the welding process, SiO2 coating is always on the weld pool surface. Only there is very narrow gap on the central region of depressed weld pool. Vapor concentrates in the lower middle part of arc. The results indicate that arc polarity area constriction and input heat increase are the main mechanism to increase weld penetration by SiO2 in AC A-TIG welding for aluminum alloy. |
关键词 | Electron beam welding Evaporation Inert gas welding Silica Alternating current activating tungsten inert gas (AC ATIG) welding Weld penetration |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding, No. 111 He-Xing Lu, Harbin, China |
EI入藏号 | 20081111146733 |
EI主题词 | Aluminum alloys |
EI分类号 | 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 802.3 Chemical Operations - 804.2 Inorganic Compounds |
来源库 | Compendex |
分类代码 | 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 802.3 Chemical Operations - 804.2 Inorganic Compounds |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/111877 |
专题 | 材料科学与工程学院 |
作者单位 | State Key laboratory of New Non-Ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Huang, Yong,Fan, Ding. Mechanism of weld penetration increased by SiO2 in AC A-TIG welding for aluminum alloy[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2008,29(1):45-49. |
APA | Huang, Yong,&Fan, Ding.(2008).Mechanism of weld penetration increased by SiO2 in AC A-TIG welding for aluminum alloy.Hanjie Xuebao/Transactions of the China Welding Institution,29(1),45-49. |
MLA | Huang, Yong,et al."Mechanism of weld penetration increased by SiO2 in AC A-TIG welding for aluminum alloy".Hanjie Xuebao/Transactions of the China Welding Institution 29.1(2008):45-49. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[Huang, Yong]的文章 |
[Fan, Ding]的文章 |
百度学术 |
百度学术中相似的文章 |
[Huang, Yong]的文章 |
[Fan, Ding]的文章 |
必应学术 |
必应学术中相似的文章 |
[Huang, Yong]的文章 |
[Fan, Ding]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论